BAKHTAR Bitumen Oxidized bitumen 95/25
Description of oxidized bitumen 95/25
BAKHTAR Bitumen Oxidized Bitumen 95/25 is Semi Solid grade of pure petroleum bitumen produced in the process of blowing hot air through an asphalt flux. Special physical properties of this grade can be used in different applications in the construction industry. BAKHTAR Bitumen Oxidized bitumen 95/25 is a petroleum bitumen which is made oxidized by bitumen 60/70 and blowing very hot air through it. The numbers refer to the midpoint of the material’s softening point and penetration relatively. The softening point value is the degrees Centigrade measured by the Ring and Ball method as determined by ASTM Standards D36. The penetration value is in 1/10 mm as determined by IP49 or ASTM- D5.
BAKHTAR Bitumen oxidized Bitumen is an industrial bitumen which has dark color, petroleum residue modified by the oxidation process. Oxidized Bitumen is produced by passing air through bitumen under controlled temperature conditions. Its ranges are from highly viscous to solid type. Blown bitumen grade has technical advantages toward the other bitumen such as durability, flexibility, water resistant and chemical stability.
BAKHTAR BITUMEN INDUSTRIAL GROUP Company guaranties the quality of BAKHTAR Bitumen Oxidized bitumen 95/25 and is ready to arrange the presence of international inspectors to check quality and quantity of the bitumen 95/25 during the production and also pre-delivery inspection before loading on container for each batch test report. BAKHTAR Bitumen Warranties that its products match the quality standards according to ASTM Standards.
Applications of oxidized bitumen 95/25
BAKHTAR Bitumen Oxidized bitumen 95/25 is applied in the chemical, fuel, paints, lacquers, varnishes, paper-pulp-board, textile processing, road construction, pavement, crack seal and repair, civil works, roofing, construction industries, sealing and insulating buildings, adhesive, construction materials additive, dust-binding, insulating and impregnating agent, make rubber and plastic products. The BAKHTAR Bitumen oxidized bitumen 95/25 is used in paving, asphalt-based paints for corrosion protection of metals, in lining public works structures, adhesives in electrical laminates, base for synthetic turf, typical uses for bitumen 95/25 is used also for water-proof application and corrosion resistance for pipe coating, Portland cement pavement, hydraulic applications, paint manufacturing, caulking, mastics, and damp proofing. Oxidized Bitumen 95/25 is applied in insulation and isolation bitumen membrane sheet. Also is utilized in Car undercoating Automobile industry is specially required for Blown Asphalt. Vehicle undercoating material is on the basis of Bitumen. Bitumen provides excellent waterproof, dust proof and noise proof for automobile undercoating.
How to use Oxidized Bitumen 95/25
BAKHTAR Bitumen Oxidized bitumen 95/25 shall be heated with double temperature against the softening point to have flow and viscosity. Before using oxidized bitumen 95/25, clean and dry the surfaces to be free of any loose particles, formwork, curing products, irregularities, slurry, and any dirt.
Storage/handling Conditions of oxidized bitumen 95/25
BAKHTAR Bitumen 95/25 is guaranteed for the period of 10 years in the conditions of multi-time heating and cooling, you can refer to MSDS for further information.
Packing of oxidized bitumen 95/25
BAKHTAR Bitumen has provided different and several types of packing formats for its products according to the customer’s requirements and conveniences. BAKHTAR Bitumen Company is the manufacturer of oxidized bitumen 95/25 in various packing types including Kraft bag, meltable plastic bag, drum, and bulk. Oxidized Bitumen 95/25 means the softening point is 95°c and penetration is 15 desi millimeters and is produced in compliance and conformity with ASTM standard and meets the following specification.
Specification of oxidized bitumen 95/25
Analysis bitumen 95/25
Bitumen 95/25 | Test method | Unit | Specification |
Specific gravity @25/25 C | ASTM D70 | (Kg/m3) | 1.05 approx. |
Penetration @ 25°c | ASTM D5 | mm/10 | 20/30 |
Softening point °c | ASTM D36 | °C | 90/100 |
Loss on heating(wt) % | ASTM D6 | Wt. % | 0.2 max |
Flashpoint °c | ASTM D92 | °C | 250 min |
Solubility is CS2(wt) % | ASTM D4 | Wt. % | 99.5 max |
Spot test | A.A.S.H.O.T102 | — | Negative |